Influence of electrolyte ageing on the Plasma Electrolytic Oxidation of aluminium
ترجمه فارسی عنوان
تاثیر پیری الکترولیتی بر اکسیداسیون الکترولیتی پلاسما از آلومینیوم
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد فناوری نانو (نانو تکنولوژی)
چکیده انگلیسی
The chemical stability of the electrolyte in Plasma Electrolytic Oxidation (PEO) has been the subject of much systematic investigation. The present study reports on experimental results on the ageing of a usual PEO electrolyte and its effect on the oxidation of the Al2214 aluminium alloy. A solution of potassium hydroxide ([KOH] = 1 g L− 1) and sodium silicate ([Na2SiO3] = 1.65 g L− 1) diluted in deionised water was either aged by running a process during 8 h at most or not. Comparison between materials treated in either solution was made next. Cross-checked experimental results from analytical chemistry, plasma diagnostics and materials science clearly evidence the effect of ageing of the electrolyte on the PEO process behaviour. The transition from arc to “soft” regime occurs earlier (from 18 min to 13 min processing time) as the electrolyte gets older. The concomitant decrease in the electrolyte electrical conductivity (from 7.5 mS cm− 1 to 6.8 mS cm− 1) is correlated with changes in the ionic species content in the electrolyte. Fast video-imaging (125 kfr/s) reveals that the micro-discharge characteristics are also sensitive since they become less numerous per area and unit time (from 220 × 103 cm− 2 s− 1 to 120 × 103 cm− 2 s− 1), exhibit shorter lifetime and have smaller sizes as the electrolyte ages. SEM observations of the as-grown coatings combined with roughness measures indicate a decrease in coating thickness (~ 20%) and roughness (~ 30%) while species from the electrolyte accumulate in the outer porous layer simultaneously with a gradual enrichment in α-Al2O3 phase in the inner compact layer (from 36% to 43%). Finally, within the PEO conditions that were used, it is shown that the ageing phenomenon of the PEO electrolyte starts to influence the process after 2 h aged.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Surface and Coatings Technology - Volume 269, 15 May 2015, Pages 36-46