عنوان انگلیسی مقاله ISI
Effect of boron addition on the oxidation resistance of silicide protective coatings: A focus on boron location in as-coated and oxidised coated niobium alloys
ترجمه فارسی عنوان
اثر افزودن بور در مقاومت به اکسیداسیون پوشش های محافظ سیلیکات: تمرکز بر محل بور در الیاف پوشش داده شده و اکسید شده آلیاژهای نایوبیوم پوشش داده شده
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فناوری نانو (نانو تکنولوژی)
چکیده انگلیسی
Multilayered silicide coatings are developed to protect Nb alloys from high temperature oxidation. Their efficiency is improved using a second halide-activated pack-cementation step consisting in a boronizing treatment. This work focuses on the location and quantification of boron in the multi-layered silicide coating in order to study the role of boron. The observations are performed on the cross sections of coated samples, in both as-coated and oxidised (Air-1200 °C-100 h) states. Characterisation of boron is performed in a FEG-SEM using a coupled WDX-EDX system. It was observed that EDX cannot be used to locate B in a matrix containing Nb, but WDX has sufficient spectral resolution to do it. The synthesis of calibration specimens (TiB2, NbB2 and (Nb0.5 Ti0.5)B2) was required for boron quantitative analysis. The analytical conditions are reported and justified. The compositions determined for borides formed in the coating were relevant with the phase diagrams and the thermodynamic data available for this system. If present in the oxidation products, boron should be in very low amounts because it was not observed during the investigation. Nevertheless, it can be suggested that for high temperature application, the formation of highly stable borides in the coating subsurface is helpful because, in case of crack formation, borides promptly form a boro-silicate glass with a low melting temperature, which is responsible for the self-healing of the oxide scale.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Surface and Coatings Technology - Volume 253, 25 August 2014, Pages 292-299
Journal: Surface and Coatings Technology - Volume 253, 25 August 2014, Pages 292-299
نویسندگان
L. Portebois, S. Mathieu, Y. Bouizi, M. Vilasi, S. Mathieu,