Tissue properties of the human vertebral body sub-structures evaluated by means of microindentation

• The anisotropy of the substructures of the human vertebral body was investigated.
• Micro-indentation test was used to evaluate indentation modulus.
• Cortical shell was found to be orthotropic.
• Trabecular bone and cortical endplates showed transversal isotropic behavior.
• Spondylophytes showed lower indentation modulus than other substructures.

PurposeThe better understanding of vertebral mechanical properties can help to improve the diagnosis of vertebral fractures. As the bone mechanical competence depends not only from bone mineral density (BMD) but also from bone quality, the goal of the present study was to investigate the anisotropic indentation moduli of the different sub-structures of the healthy human vertebral body and spondylophytes by means of microindentation.MethodsSix human vertebral bodies and five osteophytes (spondylophytes) were collected and prepared for microindentation test. In particular, indentations were performed on bone structural units of the cortical shell (along axial, circumferential and radial directions), of the endplates (along the anterio-posterior and lateral directions), of the trabecular bone (along the axial and transverse directions) and of the spondylophytes (along the axial direction). A total of 3164 indentations down to a maximum depth of 2.5 µm were performed and the indentation modulus was computed for each measurement.ResultsThe cortical shell showed an orthotropic behavior (indentation modulus, Ei, higher if measured along the axial direction, 14.6±2.8 GPa, compared to the circumferential one, 12.3±3.5 GPa, and radial one, 8.3±3.1 GPa). Moreover, the cortical endplates (similar Ei along the antero-posterior, 13.0±2.9 GPa, and along the lateral, 12.0±3.0 GPa, directions) and the trabecular bone (Ei= 13.7±3.4 GPa along the axial direction versus Ei=10.9±3.7 GPa along the transverse one) showed transversal isotropy behavior. Furthermore, the spondylophytes showed the lower mechanical properties measured along the axial direction (Ei=10.5±3.3 GPa).ConclusionsThe original results presented in this study improve our understanding of vertebral biomechanics and can be helpful to define the material properties of the vertebral substructures in computational models such as FE analysis.

Figure optionsDownload high-quality image (325 K)Download as PowerPoint slide