Closure mechanisms in Al-Si-Mg cast alloys and long-crack to small-crack corrections
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی مکانیک
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Crack growth behavior of small and long cracks has been a subject of much research; the differences observed in the growth response were largely attributed to crack closure. In this study, cast Al-Si-Mg alloys of various residual stress levels and Si content/morphology were investigated, and the dominant closure mechanisms were identified. The near-threshold fatigue crack growth behavior of the alloys is controlled by two types of closure: residual stress-induced (due to residual stresses introduced during heat treatment) and microstructure/roughness-induced (due to variations in Si content/morphology). These closure mechanisms were individually discussed and closure corrective techniques were applied to long crack growth results. The near-threshold closure corrected long crack growth data compare favorably with small crack growth data.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Fatigue - Volume 27, Issues 10â12, OctoberâDecember 2005, Pages 1463-1472
Journal: International Journal of Fatigue - Volume 27, Issues 10â12, OctoberâDecember 2005, Pages 1463-1472
نویسندگان
Diana A. Lados, Diran Apelian, Paul C. Paris, J. Keith Donald,