What is fatigue damage? A view point from the observation of low cycle fatigue process
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی مکانیک
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: What is fatigue damage? A view point from the observation of low cycle fatigue process What is fatigue damage? A view point from the observation of low cycle fatigue process](/preview/png/9703940.png)
چکیده انگلیسی
Fatigue damage requires to be expressed in terms of a crack. This will be revealed by several items of experimental evidence. First, observations on a medium carbon steel that relate to the initiation zones and the propagation of small cracks subjected to low cycle fatigue, will be presented; these observations being based on surface replica studies. It will be shown that the Coffin-Manson high-strain, low-cycle, fatigue relationship is substantially the same as a crack growth law. Second, the effect of prior fatigue history on the growth rate of a small crack is investigated systematically using special specimens containing an artificial small hole of various diameters, i.e. 40, 100 and 200 μm. Prior fatigue history is shown to have little influence on the crack growth rate in the high-strain fatigue regime. Third, it will be revealed that the loss of fracture ductility after strain cycling in high-strain fatigue tests is attributable to the existence of small surface cracks. The loss of fracture ductility depends on the crack length l. If l is larger than a critical length l(c), the fatigue crack causes macroscopic shear fracture in a tensile test following strain cycling. On the other hand, if l is smaller than l(c), the tensile fracture surfaces are of the cup-and-cone type. For 70/30 brass, l(c) is about 400 μm. Thus, fatigue damage models which ignore the reality of fatigue damage as expressed in terms of cracks should not be used for fatigue life predictions.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Fatigue - Volume 27, Issue 8, August 2005, Pages 991-1005
Journal: International Journal of Fatigue - Volume 27, Issue 8, August 2005, Pages 991-1005
نویسندگان
Y. Murakami, K.J. Miller,