عنوان انگلیسی مقاله ISI
Electrochemical evaluation of La0.6Sr0.4CoO3-La0.45Ce0.55O2 composite cathodes for anode-supported La0.45Ce0.55O2-La0.9Sr0.1Ga0.8Mg0.2O2.85 bilayer electrolyte solid oxide fuel cells
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
الکتروشیمی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Electrochemical evaluation of La0.6Sr0.4CoO3-La0.45Ce0.55O2 composite cathodes for anode-supported La0.45Ce0.55O2-La0.9Sr0.1Ga0.8Mg0.2O2.85 bilayer electrolyte solid oxide fuel cells Electrochemical evaluation of La0.6Sr0.4CoO3-La0.45Ce0.55O2 composite cathodes for anode-supported La0.45Ce0.55O2-La0.9Sr0.1Ga0.8Mg0.2O2.85 bilayer electrolyte solid oxide fuel cells](/preview/png/9761717.png)
چکیده انگلیسی
The electrochemical properties of porous composite cathodes of La0.6Sr0.4CoO3 (LSC) and La0.45Ce0.55O2 (LDC) in anode supported lanthanum-doped ceria (LDC)/lanthanum gallate (LSGM) bilayer electrolyte single cells have been investigated. The composite cathodes with different LDC and LSC contents were in contact with the LSGM layer in the single cells. Comparing with the pure LSC cathode, the interfacial resistance decreased upon the addition of LDC and the optimum content of LDC was 50 wt.%. The variation in ohmic resistance suggests that the composite cathode can suppress Co diffusion from the cathode into the LSGM electrolyte during the firing of the composite cathode onto the electrolyte. The composite cathode with 50 wt.% LDC showed an ohmic resistance near to the calculated resistance of an electrolyte film. For the pure LSC cathode, the optimum firing temperature was about 1150 °C, at which both the electrolyte resistance and interface resistance were the smallest. The cathodic interfacial resistance was effectively reduced for the composite cathodes, especially for the cathode with 50 wt.% LDC, which might be due to the suppressing of sintering and the growth of LSC particles from LDC particles during the firing onto the electrolyte. The complicated effects of the composite cathode on the interfacial resistance and ohmic resistance resulted in the best single cell performance at 650 °C with a 50 wt.% LDC composite cathode, and the best cell performance above 700 °C on the single cell with pure LSC cathode.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Solid State Ionics - Volume 176, Issues 7â8, 28 February 2005, Pages 655-661
Journal: Solid State Ionics - Volume 176, Issues 7â8, 28 February 2005, Pages 655-661
نویسندگان
Zhonghe Bi, Mojie Cheng, Yonglai Dong, Hejin Wu, Yunchuan She, Baolian Yi,