Radiation damages and bubble formation of ion implanted furan-resin-derived carbon

The Xe+-implanted specimens were subjected to annealing of re-heat-treatment at 3000 °C. After the annealing, the bubbles were lost in the interior of specimens by cross-sectional SEM observations. Moreover, on the implanted surfaces appeared big bubbles, which were not presented on the implanted surface before annealing. The sizes of these big bubbles were about 2-10 μm. Using Raman spectroscopy, we observed that on the surface of the big bubbles the structure was re-well-graphitized. On the surface of non-bubbled areas it was less graphitized. Thus annealing provided a restoration of the structural, but much effective only on the bubble surfaces.