Ion-beam formation of nanopores and nanoclusters in SiO2
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سطوح، پوششها و فیلمها
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
We studied nanopores and nanoclusters formation in thermally oxidized silicon wafers (SiO2/Si) by means of ion-beam technique. RBS, SEM, TEM and TED were used to characterize the SiO2 layers after the ion-beam processing. Nanopores were formed by high-energy Kr ions irradiation followed by chemical etching of latent tracks zones in SiO2 matrix. Holes with diameters of â¼10-15Â nm and length/diameter ratios of up to 22 have been etched through the SiO2 film. The results of computer simulation of the track formation processes in SiO2 based on the modified thermal spike model are also presented. Calculated radiuses of molten regions along swift Kr ion trajectories in fused silica have been compared with etched tracks dimensions. Nanoclusters were formed by co-implantation of As and In ions followed by high-energy Kr ions irradiation and thermal annealing. The high-energy Kr ions irradiation as a thermal annealing alternative was carried out to induce nanoclusters formation in swift ions tracks zones. TEM investigations of annealed samples demonstrate the presence of amorphous nanoclusters located at the depth of 40-190Â nm. Their sizes vary from â¼2.5 to â¼6Â nm. No influence of swift ion irradiation on the oriented precipitation of dopants (In+As) in the tracks region was revealed.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Vacuum - Volume 78, Issues 2â4, 30 May 2005, Pages 361-366
Journal: Vacuum - Volume 78, Issues 2â4, 30 May 2005, Pages 361-366
نویسندگان
F.F. Komarov, L.A. Vlasukova, O.M. Milchanin, P.I. Gaiduk, V.N. Yuvchenko, S.S. Grechnyi,