Characterization of fatigue crack growth, damage mechanisms and damage evolution of the nickel-based superalloys MAR-M247 CC (HIP) and CM-247 LC under thermomechanical fatigue loading using in situ optical microscopy
Keywords: سوپرآلیاژ بر پایه نیکل; Thermomechanical fatigue crack growth; Nickel-based superalloy; Digital image processing;