عنوان انگلیسی مقاله ISI
Effect of alumina-silica-zirconia eutectic ceramic thermal barrier coating on the low cycle fatigue behaviour of cast polycrystalline nickel-based superalloy at 900 °C
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فناوری نانو (نانو تکنولوژی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effect of alumina-silica-zirconia eutectic ceramic thermal barrier coating on the low cycle fatigue behaviour of cast polycrystalline nickel-based superalloy at 900 °C Effect of alumina-silica-zirconia eutectic ceramic thermal barrier coating on the low cycle fatigue behaviour of cast polycrystalline nickel-based superalloy at 900 °C](/preview/png/5465478.png)
چکیده انگلیسی
Cylindrical specimens of nickel-based superalloy Inconel 713LC in an as-cast condition and coated with a thermal barrier coating (TBC) system consisting of a CoNiCrAlY bond coat and an eutectic ceramic alumina-silica-zirconia top coat were cyclically loaded under strain control at 900 °C in air. TBC was deposited using atmospheric plasma spray and water-stabilised plasma spray techniques for the bond coat and the top coat, respectively. The microstructure of the substrate material and the TBC was characterised and the hardness of TBC was measured. The cyclic stress-strain response and fatigue life of both materials were assessed. The stress response of the TBC-coated superalloy is lower than the uncoated superalloy. The detrimental effect of TBC on the Basquin curve is documented. The specimen section and fracture surface observations revealed fatigue damage mechanisms in both the TBC-coated and uncoated specimens, and that finding helps explain the differences in the fatigue behaviour of both materials.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Surface and Coatings Technology - Volume 318, 25 May 2017, Pages 374-381
Journal: Surface and Coatings Technology - Volume 318, 25 May 2017, Pages 374-381
نویسندگان
Karel ObrtlÃk, Ladislav Äelko, TomáÅ¡ Chráska, Ivo Å ulák, Pavel GejdoÅ¡,