Simultaneous in situ monitoring of acrylic acid polymerization reaction on N-carboxymethyl chitosan using multidetectors: Formation of a new bioadhesive and gastroprotective hybrid particle
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
بیومتریال
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Chitosan and polyacrylic acid (PAA) both have weak, short-lasting bioadhesive properties; therefore, a hybrid particle composed of a chitosan derivative and PAA could be used as a new bioadhesive agent. Using simultaneous in-situ monitoring with a multidetection system, N-carboxymethyl chitosan was ionically bonded to acrylic acid and then polymerized using potassium persulphate as the initiator (N-CMCA-Dh of 165 nm). The PAA on N-CMCA was crosslinked using N,N-methylene-bisacrylamide (N-CMCAC-Dh of 141 nm). During polymerization, the solution developed a milky white appearance, and polymerization kinetics was determined to be 3.2 Ã 10â3 ± 4.0 Ã 10â6 mmol/min. The reaction for PAA alone was 1.7 times faster than that of the hybrid system. The particles showed an increase in thermal stability and reduction of thermal-mass loss compared with the N-CMC alone. The N-CMCAC particles showed the highest bioadhesion onto the stomach. The gastroprotection index of N-CMChAC particles against ethanol/HCl-induced ulcers in mice was 68.2 ± 6.4%. Similar results were observed for omeprazole (74.2 ± 5.3%). The particles obtained in this work have potential for use in drug delivery to the stomach, perhaps to aid in treating ulceration and inflammation, and can be used as a system for the prevention of ethanol-induced ulcers.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: C - Volume 31, Issue 3, 8 April 2011, Pages 677-682
Journal: Materials Science and Engineering: C - Volume 31, Issue 3, 8 April 2011, Pages 677-682
نویسندگان
Oscar D'Agostini-Junior, Carmen Lucia Petkowicz, Angelica Garcia Couto, Sergio Faloni de Andrade, Rilton Alves Freitas,