عنوان انگلیسی مقاله ISI
Persistent photoluminescence emission from SrTa2O6:Pr3+ phosphor prepared at different temperatures
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Persistent photoluminescence emission from SrTa2O6:Pr3+ phosphor prepared at different temperatures Persistent photoluminescence emission from SrTa2O6:Pr3+ phosphor prepared at different temperatures](/preview/png/10624631.png)
چکیده انگلیسی
Phosphors with persistent emission are of interest for security and emergency signage, and medical diagnosis. Three SrTa2O6:Pr3+phosphor samples with persistent emission were prepared by solid state reaction at 1200, 1400 and 1500 °C. Structural crystallization was shown to improve with an increase in temperature as identified by X-ray diffraction. The scanning electron microscopy images showed that the particles of the phosphor were agglomerated and co-melting was induced by increasing the synthesis temperature. The ion distribution in the phosphors was determined using the time of flight secondary ion mass spectroscopy. The red emission was obtained from the D2â3H4 and the 3P0â3H6 transitions at 608 and 619 nm, respectively. The main absorption occurred at 225 nm (5.5 eV), and the band gap (Eg) calculations confirmed that it corresponds to band-to-band excitation. Another excitation due to charge transfer at 300 nm was also obtained which makes the phosphor suitable to be used in red light emitting diodes. The persistent emission time parameters (260-296 s) were calculated from the phosphorescence decay curves using the second order exponential decay equation. The corresponding electron trapping centers were determined using the thermoluminescence spectroscopy, and the activation energy was determined using the initial rise method.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 41, Issue 7, August 2015, Pages 8828-8836
Journal: Ceramics International - Volume 41, Issue 7, August 2015, Pages 8828-8836
نویسندگان
L.L. Noto, M.Y.A. Yagoub, O.M. Ntwaeaborwa, H.C. Swart,