Microstructure and microtexture in laser-dressed alumina grinding wheel material
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Microstructure and microtexture in laser-dressed alumina grinding wheel material Microstructure and microtexture in laser-dressed alumina grinding wheel material](/preview/png/10626461.png)
چکیده انگلیسی
Alumina grinding wheels when laser dressed with a high-power laser induce change in the morphology of the wheel surface. The altered grain structure on the surface of the wheel gives laser dressing advantage over conventional mechanical methods. Morphological modification during laser dressing is strongly influenced by the microstructure formed during the rapid solidification process. Microstructure depends mainly on the cooling rates amongst many other factors related to the laser processing conditions. Using a two-color based pyrometer temperature measurement setup the cooling rates were estimated during the laser dressing process. Orientation imaging microscopy (OIM) was used to determine the grain orientations in the resolidified layer on the dressed surface. Cooling rates and the OIM combined, indicate a preferred orientation of grains along the (110) planes. This preferred orientation can be a reason for the formation of grains with multi-faceted surfaces having cutting edges and vertices, for grinding operation. OIM and cooling results also show existence of a competitive growth mechanism for the grains in the dressed layer.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 31, Issue 4, 2005, Pages 621-629
Journal: Ceramics International - Volume 31, Issue 4, 2005, Pages 621-629
نویسندگان
Abhijeet A. Khangar, Edward A. Kenik, Narendra B. Dahotre,