Pitting corrosion of the laser surface melted Alloy 600
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی انرژی
انرژی هسته ای و مهندسی
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
The effect of laser surface melting (LSM) on the resistance to pitting corrosion of Ni-base Alloy 600 was investigated by a potentiodynamic polarization test in 1 M NaCl solutions at pH values of 4 and 10 at temperatures of 30, 60 and 90 °C. The pitting potentials of Alloy 600 were markedly increased by the LSM process, when compared with those of the non-laser treated Alloy 600. From the microscopic examination after the corrosion test, it was found that the pitting was initiated at the junction between a TiN inclusion and the matrix, possibly at the site of a sulfide physically associated with the TiN inclusion. The homogeneous micro-structure associated with the reduction of the inclusion size during the LSM process could be attributed to the improvement of the pitting corrosion properties in the LSM Alloy 600.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Nuclear Materials - Volume 336, Issue 1, 1 January 2005, Pages 65-72
Journal: Journal of Nuclear Materials - Volume 336, Issue 1, 1 January 2005, Pages 65-72
نویسندگان
Yun Soo Lim, Joung Soo Kim, Hyuk Sang Kwon,