عنوان انگلیسی مقاله ISI
The influence of pulse plating parameters on structure and properties of Ni-W-TiO2 nanocomposite coatings
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فناوری نانو (نانو تکنولوژی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: The influence of pulse plating parameters on structure and properties of Ni-W-TiO2 nanocomposite coatings The influence of pulse plating parameters on structure and properties of Ni-W-TiO2 nanocomposite coatings](/preview/png/10668019.png)
چکیده انگلیسی
In the present work, Ni-W-TiO2 nanocomposite coatings were produced on low carbon steel substrates by means of pulse electrodeposition. To this end, the effects of frequency, duty cycle, current type, and presence of TiO2 nano-particles on structure and properties of the coatings were investigated. Microstructure of the coatings and dispersion of TiO2 nano-particles were studied by scanning electron microscopy (SEM). Crystallite size was calculated using X-ray diffraction patterns by the Scherrer equation. Corrosion performance of the coatings in 0.5Â M NaCl as the corrosive solution was investigated by the potentiodynamic polarization method. Finally, the micro-hardness of the coatings was assessed using a Vickers micro-indenter. The results indicated that the pulse frequency of 1000Â Hz, duty cycle of 60%, average current density of 10Â A/dm2, and TiO2 nano-particle concentration of 10Â g/L were the optimum plating conditions. The amount of TiO2 nano-particles incorporated into the coating that were produced under the optimum plating conditions was 1.47Â wt.%; also, the crystallite size of this coating was 4Â nm and the micro-hardness was 780Â Hv.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Surface and Coatings Technology - Volume 259, Part C, 25 November 2014, Pages 393-400
Journal: Surface and Coatings Technology - Volume 259, Part C, 25 November 2014, Pages 393-400
نویسندگان
H. Goldasteh, S. Rastegari,