Structural and magnetic properties of cadmium substituted Ni-Al ferrites

Nickel Cadmium Aluminum Ferrites with the general formula Ni1−xCdxAl0.6Fe1.4O4 where x=0, 0.25, 0.50 and 0.75 were prepared through standard double sintering reaction method. The crystallography, surface morphology and magnetic properties were studied by X-ray diffractometer (XRD), Scanning Electron Microscope (SEM) and Vibrating Sample Magnetometer (VSM), respectively. The expected single phase spinel structure was confirmed by XRD analysis. Lattice parameter and X-ray density were increased monotonically by increasing Cd concentration due to the larger ionic radii of the cadmium ion. Surface topography of the samples consists of fine cubical shape microstructures. The average grain size increased with increase in cadmium concentration. The saturation magnetization was found to be increased with increase in cadmium content up to x=0.50 and then decreased with further increasing cadmium concentration for x=0.75.