Ortho-para hydrogen conversion characteristics of amorphous and mesoporous Cr2O3 powders at a temperature of 77 K
موضوعات مرتبط
مهندسی و علوم پایه شیمی الکتروشیمی
پیش نمایش صفحه اول مقاله
Ortho-para hydrogen conversion characteristics of amorphous and mesoporous Cr2O3 powders at a temperature of 77 K
چکیده انگلیسی


• Mesoporous Cr2O3 catalysts were prepared for ortho-para hydrogen conversion.
• Catalysts have high BET surface area and show nanowire array morphology.
• Surface area and morphology play an important role in spin conversion rate.

In this study, mesoporous Cr2O3 catalysts are prepared by use of the hard template method using mesoporous silica (SBA-15) as template, the prepared catalysts were characterized, and investigated for ortho to para hydrogen. The Cr2O3 catalysts at post-treated temperature at 150 °C have the largest BET surface area of 230 m2 g−1, and the length and diameter of the particles are 2 μm and 5 nm, respectively. The highest spin conversion from ortho to para hydrogen was observed for the mesoporous Cr2O3 catalysts with the largest surface area post-treated at 150 °C in the range from 150 to 300 °C. The nanowire array morphology of the powders was maintained at the post-treatment temperature ranges of 150 and 200 °C. However, when temperature increased up to 300 °C, the nanowire array morphology disappeared. It was showed that the spin conversion process was strongly dependent on various factors such as BET surface area, calcination temperature and morphology of mesoporous Cr2O3 catalysts.