![عکس صفحه اول مقاله: Preparation and characterization of Ba0.5Sr0.5Fe0.9Ni0.1O3−δ–Sm0.2Ce0.8O1.9 compose cathode for proton-conducting solid oxide fuel cells Preparation and characterization of Ba0.5Sr0.5Fe0.9Ni0.1O3−δ–Sm0.2Ce0.8O1.9 compose cathode for proton-conducting solid oxide fuel cells](/preview/png/1271297.png)
A cobalt-free Ba0.5Sr0.5Fe0.9Ni0.1O3−δ–Sm0.2Ce0.8O1.9 (BSFN–SDC) composite was employed as a cathode for proton-conducting solid oxide fuel cells (H-SOFCs) using BaZr0.1Ce0.7Y0.2O3−δ (BZCY) as the electrolyte. The chemical compatibility between BSFN and SDC was evaluated. The XRD results showed that BSFN was chemically compatible with SDC after co-fired at 1100 °C for 5 h. The thermal expansion coefficient (TEC) of BSFN–SDC, which showed a reasonably reduced value (16.08 × 10−6 K−1), was effectively decreased due to Ce0.8Sm0.2O1.9 (SDC) added. A single cell of Ni–BZCY/Ni–BZCY/BZCY/BSFN–SDC with a 25-μm-thick BZCY electrolyte membrane exhibited excellent power densities as high as 361.8 mW cm−2 at 700 °C with a low polarization resistance of 0.174 Ω cm2. The excellent performance implied that the cobalt-free BSFN–SDC composite was a promising alternative cathode for H-SOFCs.
Journal: International Journal of Hydrogen Energy - Volume 37, Issue 12, June 2012, Pages 9830–9835