The La2−xTixMgNi9 (x = 0.1, 0.2, 0.3, 0.4) alloys were prepared by magnetic levitation melting under Ar atmosphere. The effects of partial substitution Ti for La on the phase structures, hydrogen-storage properties and electrochemical characteristics of the alloys were investigated systematically. For La2−xTixMgNi9 (x = 0.1, 0.2, 0.3, 0.4) alloys, LaNi5, LaNi3 and LaMg2Ni9 are the main phases, the maximum hydrogen-storage capacity is 1.51, 1.36, 1.35 and 1.22 wt%, respectively. The absorption–desorption plateau pressure of the alloys first decreases and then increases with increase of Ti content, and the La1.8MgTi0.2Ni9 alloy has the lowest absorption–desorption plateau pressure. The discharge voltage of the alloy electrodes rises with increasing the amount of Ti content. The La1.8Ti0.2MgNi9 alloy electrode presents good electrochemical performance.
Journal: International Journal of Hydrogen Energy - Volume 34, Issue 11, June 2009, Pages 4827–4832