Enhanced hydrogen sorption in single walled carbon nanotube incorporated MIL-101 composite metal–organic framework

Metal–Organic Frameworks (MOFs) have emerged as potential hydrogen storage media due to their high surface area, pore volume and adjustable pore sizes. The large void space generated by cages in MOFs is not completely utilized for hydrogen storage application owing to weak interactions between the walls of MOFs and H2 molecules. These unutilized volumes in MOFs can be effectively utilized by incorporation of other microporous materials such as single walled carbon nanotubes into the pores of MOFs which could effectively tune the pore size and pore volume of the material towards hydrogen sorption. Single walled carbon nanotubes (SWNT) incorporated MIL-101 composite MOF material (SWNT@MIL-101) was synthesized by adding purified single walled carbon nanotube (SWNT) in situ during the synthesis of MIL-101. The powder X-ray diffraction patterns of SWNT@MIL-101 showed the structure of MOF was not disturbed by SWNT incorporation. Hydrogen sorption capacities of MIL-101 was observed to increase from 6.37 to 9.18 wt% at 77 K up to 60 bar and from 0.23 to 0.64 wt% at 298 K up to 60 bar. The increment in the hydrogen uptake capacities of composite MOF materials was attributed to the decrease in the pore size and enhancement of micropore volume of MIL-101 by single walled carbon nanotube incorporation.

► Preparation of hybrid MOF material by incorporation of purified SWNT in MIL-101.
► Utilization of unused space in high surface area MOFs by micropore volume enhancement.
► Enhancement of hydrogen sorption at 77 K and 298 K in MIL-101 by SWNT incorporation.
► DFT calculations of CO2 adsorption isotherms at 273 K in MOF material to confirm ultramicropore formation.