![عکس صفحه اول مقاله: Effect of ball milling time on the hydrogen storage properties of TiF3-doped LiAlH4 Effect of ball milling time on the hydrogen storage properties of TiF3-doped LiAlH4](/preview/png/1283066.png)
In the present work, the catalytic effect of TiF3 on the dehydrogenation properties of LiAlH4 has been investigated. Decomposition of LiAlH4 occurs during ball milling in the presence of 4 mol% TiF3. Different ball milling times have been used, from 0.5 h to 18 h. With ball milling time increasing, the crystallite sizes of LiAlH4 get smaller (from 69 nm to 43 nm) and the dehydrogenation temperature becomes lower (from 80 °C to 60 °C). Half an hour ball milling makes the initial dehydrogenation temperature of doped LiAlH4 reduce to 80 °C, which is 70 °C lower than as-received LiAlH4. About 5.0 wt.% H2 can be released from TiF3-doped LiAlH4 after 18 h ball milling in the range of 60 °C–145 °C (heating rate 2 °C min−1). TiF3 probably reacts with LiAlH4 to form the catalyst, TiAl3. The mechanochemical and thermochemical reactions have been clarified. However, the rehydrogenation of LiAlH4/Li3AlH6 can not be realized under 95 bar H2 in the presence of TiF3 because of their thermodynamic properties.
Journal: International Journal of Hydrogen Energy - Volume 34, Issue 19, October 2009, Pages 8079–8085