کد مقاله | کد نشریه | سال انتشار | مقاله انگلیسی | نسخه تمام متن |
---|---|---|---|---|
1286060 | 1497912 | 2016 | 8 صفحه PDF | دانلود رایگان |
عنوان انگلیسی مقاله ISI
Highly redox-resistant solid oxide fuel cell anode materials based on La-doped SrTiO3 by catalyst impregnation strategy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
الکتروشیمی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Highly redox-resistant solid oxide fuel cell anode materials based on La-doped SrTiO3 by catalyst impregnation strategy Highly redox-resistant solid oxide fuel cell anode materials based on La-doped SrTiO3 by catalyst impregnation strategy](/preview/png/1286060.png)
چکیده انگلیسی
An anode backbone using 40 wt% (ZrO2)0.89(Sc2O3)0.1(CeO2)0.01 (SSZ)-Sr0.9La0.1TiO3 (SLT) cermet was prepared for SSZ electrolyte-supported SOFC single cells. 15 mgcmâ2 Ce0.9Gd0.1O2 (GDC) was impregnated to totally cover the SSZ-SLT anode backbone surface acting as a catalyst, and the cell voltage achieved 0.865 V at 200 mAcmâ2 using (La0.75Sr0.25)0.98MnO3 (LSM)-SSZ cathode in 3%-humidified hydrogen fuel at 800 °C. Cell performance was substantially improved from 0.865 V to >0.97 V when 0.03 mgcmâ2 Pd or Ni was further incorporated as a secondary catalyst into the anode layer. 50 redox cycles were performed to investigate redox stability of this high performance anode. It was found that even after the 50 redox cycle long-term degradation test, cell voltage at 200 mAcmâ2 was retained around 0.94 V, higher than the cell performance using the conventional Ni-SSZ cermet anode. The catalytically-active reaction sites at ceria-Pd or ceria-Ni may account for the excellent performance, and the extremely low metal catalyst concentration prevent serious metal aggregation in achieving excellent redox stability.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Power Sources - Volume 320, 15 July 2016, Pages 180-187
Journal: Journal of Power Sources - Volume 320, 15 July 2016, Pages 180-187
نویسندگان
X. Shen, K. Sasaki,