Sulfonic-functionalized heteropolyacid–SiO2 nanoparticles were synthesized by grafting and oxidizing of a thiol-silane compound onto the heteropolyacid–SiO2 nanoparticle surface. The surface functionalization was confirmed by solid-state NMR spectroscopy. The composite membrane containing the sulfonic-functionalized heteropolyacid–SiO2 nanoparticles was prepared by blending with Nafion® ionomer. TG–DTA analysis showed that the composite membrane was thermally stable up to 290 °C. The DMFC performance of the composite membrane increased the operating temperature from 80 to 200 °C. The function of the sulfonic-functionalized heteropolyacid–SiO2 nanoparticles was to provide a proton carrier and act as a water reservoir in the composite membrane at elevated temperature. The power density was 33 mW cm−2 at 80 °C, 39 mW cm−2 at 160 °C and 44 mW cm−2 at 200 °C, respectively.
Journal: Journal of Power Sources - Volume 158, Issue 1, 14 July 2006, Pages 137–142