Effects of (LaSr)(CoFeCu)O3−δ cathodes on the characteristics of intermediate temperature solid oxide fuel cells

In this study, Cu2+ ions doped La0.6Sr0.4Co0.2Fe0.8O3−δ cathodes are prepared for use in solid oxide fuel cells (SOFCs). The maximum electrical conductivities of the La0.6Sr0.4Co0.2Fe0.7Cu0.1O3−δ (438 S cm−1) and the La0.6Sr0.4Co0.1Fe0.8Cu0.1O3−δ (340 S cm−1) discs are higher than that of the La0.6Sr0.4Co0.2Fe0.8O3−δ disc (LSCF; 81 S cm−1) sintered at 1100 °C. The substitution of Cu2+ over Fe3+ leads to a higher coefficients of thermal expansion (CTE), while the replacement of Co3+ by Cu2+ results in a lower CTE. Single cells with the La0.6Sr0.4Co0.2Fe0.8O3−δ, La0.6Sr0.4Co0.2Fe0.7Cu0.1O3−δ, and La0.6Sr0.4Co0.1Fe0.8Cu0.1O3−δ cathodes operating at 650 °C and 550 °C show similar ohmic resistance (R0) values while the polarization resistance (RP) values of the cells with the La0.6Sr0.4Co0.2Fe0.7Cu0.1O3−δ and a0.6Sr0.4Co0.1Fe0.8Cu0.1O3−δ cathodes are slightly lower than that of the single cell with the La0.6Sr0.4Co0.2Fe0.8O3−δ cathode, indicating that the Cu2+-doped LSCF cathode exhibits a greater electrochemical catalytic activity for oxygen reduction. Maximum power densities of the cells with the La0.6Sr0.4Co0.2Fe0.8O3−δ, La0.6Sr0.4Co0.2Fe0.7Cu0.1O3−δ, and La0.6Sr0.4Co0.1Fe0.8Cu0.1O3−δ cathodes operating at 700 °C read respectively 1.07, 1.15, and 1.24 W cm−2. It is evident that the doping of Cu2+ ions in LSCF is beneficial to the electrochemical performance of the cells.

► Cu2+ ions doped La0.6Sr0.4Co0.2Fe0.8O3−δ cathodes were prepared for used in solid oxide fuel cell.
► The maximum electrical conductivities of Cu-doped LSCF discs are higher than that of LSCF.
► The dopant of Cu2+ ions in LSCF is beneficial to the electrochemical performance of cells.