A multilayer coating of dense SiC alternated with porous Si–Mo for the oxidation protection of carbon/carbon silicon carbide composites

In order to improve the oxidation behavior of carbon/carbon silicide carbide composites prepared by liquid silicon infiltration of carbon/carbon porous preforms, a multilayer coating of dense SiC alternated with porous Si–Mo was prepared by chemical vapor deposition combined with slurry painting. Oxidation test showed that weight loss of the coated sample was only 0.25% after 150 h oxidation in air at 1673 K. And the coated sample gained weight in the course of 46 cycles of thermal shock test between 1673 K and 373 K. The coating remained intact during the two kinds of tests and no obvious failure was found. The excellent oxidation protective ability and thermal shock resistance of the SiC/Si–Mo coating can be attributed to the alternated structure.