Development of poly(lactic acid) nanostructured membranes for the controlled delivery of progesterone to livestock animals

Solution blow spinning (SBS) is a novel technology feasible to produce nanostructured polymeric membranes loaded with active agents. In the present study, nanofibrous mats of poly(lactic acid) (PLA) loaded with progesterone (P4) were produced by SBS at different P4 concentrations. The spun membranes were characterized by scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and Fourier-transform infrared spectroscopy (FTIR). The in vitro releasing of P4 was evaluated using high-performance liquid chromatography (HPLC). Interactions between progesterone and PLA were confirmed by rheological measurements of the PLA/P4 solutions and in the spun mats by microscopy (SEM), thermal (DSC) and spectral (FTIR) analyses. SEM micrographs provided evidences of a smooth and homogeneous structure for nanostructured membranes without progesterone crystals on fiber surface. FTIR spectroscopy indicated miscibility and interaction between the ester of PLA and the ketone groups of the P4 in the nanofibers. X-ray analysis indicated that the size of PLA crystallites increased with progesterone content. Finally, by in vitro release experiments it was possible to observe that the progesterone releasing follows nearly first-order kinetics, probably due to the diffusion of hormone into PLA nanofibers.

► Nanofibers of PLA loading with progesterone were prepared via solution blow spinning.
► Their morphology, FTIR, and XRD and DSC characterization were analyzed.
► Fibers of PLA/progesterone with diameters from 280 to 440 nm were obtained.
► The effect of progesterone content in fiber properties was studied.