![عکس صفحه اول مقاله: A novel surface modification on calcium polyphosphate scaffold for articular cartilage tissue engineering A novel surface modification on calcium polyphosphate scaffold for articular cartilage tissue engineering](/preview/png/1430411.png)
The surface of porous three-dimensional (3D) calcium polyphosphate (CPP) scaffold was modified by treatment of quenching-after-sintering in the fabrication process. Scanning electron microscopic examination and degradation tests confirmed a new type of surface modification. A rotary-shaking culture was compared to that of a stationary culture and the results showed that rotary shaking led to enhanced extracellular matrices (ECM) secretion of both proteoglycans and collagen. Rotary-shaking cultured results showed that the quenching-treated CPP scaffold produced a better cartilage tissue, with both proteoglycans and collagen secretions enhanced, than the air-cooled-after-sintering scaffolds. Moreover, β-CPP scaffolds were better for the ECM secretion of both proteoglycans and collagen than the β-CPP + γ-CPP multiphase scaffold. However, the multiphase scaffold led to higher growth rate than that of β-CPP scaffold; the quenching-after-sintering treatment reversed this. In addition, the ECM secretions of both proteoglycans and collagen in the quenching-treated β-CPP scaffold were higher than those in the air-cooled one. Thus, the novel treatment of quenching-after-sintering has shown merits to the porous 3D CPP scaffolds for articular cartilage tissue engineering.
Journal: Materials Science and Engineering: C - Volume 27, Issue 1, January 2007, Pages 127–134