Characteristics of Na–Mg double salt for high-temperature CO2 sorption
موضوعات مرتبط
مهندسی و علوم پایه مهندسی شیمی مهندسی شیمی (عمومی)
پیش نمایش صفحه اول مقاله
Characteristics of Na–Mg double salt for high-temperature CO2 sorption
چکیده انگلیسی


• Na–Mg double salt having unique CO2 sorption behavior at high-temperature.
• Very high CO2 sorption uptake at high-temperature, especially around 375 °C.
• Excellent cyclic stability and fast sorption/desorption kinetics.
• In situ XRD analysis implying CO2 reacts with MgO and Na2CO3 to form Na2Mg(CO3)2.

A novel high temperature CO2 sorbent, Na–Mg double salt, was prepared by a precipitation method. Thermogravimetric analysis was used to measure the thermal stability and to investigate the CO2 sorption behavior at high temperatures. The prepared Na–Mg double salt showed unique CO2 sorption characteristics in the temperature range of 300–500 °C. A remarkably high CO2 sorption uptake of 3.48 mol/kg (15.3 wt%) was measured at 375 °C and was maintained during repeated sorption/desorption cycles. Electronic microscopy and X-ray diffraction were used to determine the Na–Mg double salt morphology and structure, respectively. The elemental composition ratio in the Na–Mg double salt was characterized by inductively coupled plasma atomic emission spectroscopy and an elemental analysis. In situ X-ray diffraction analysis revealed that the CO2 sorption mechanism was based on the reaction of CO2 with MgO and Na2CO3 in the double salt to form Na2Mg(CO3)2. In addition to the high CO2 sorption uptake and good cyclic stability, the Na–Mg double salt showed exceptionally fast sorption and desorption.