Asymmetric perovskite membranes have an attractive potential in the application of O2/N2 gas separation for future membrane-based power plants using oxyfuel technology. In this study – a metal-supported membrane structure with a thin-film perovskite layer and porous ceramic interlayers was developed. Porous NiCoCrAlY sintered at 1225 °C in H2 was selected as the substrate based on a sufficient permeability and corrosion resistance in co-firing conditions. According to the oxidation behaviour of NiCoCrAlY, the temperature for co-firing of the substrate and the interlayers was defined as 1100 °C for 5 h in air. Two interlayers of La0.58Sr0.4Co0.2Fe0.8O3−δ were applied by screen printing. The top layer was deposited by magnetron sputtering with a thickness of 3.8 μm. While gas-tightness was improved considerably, significant air-leakage was still detected. In summary, the successful development of a metal-perovskite-composite is shown, which acts as a basis for further development of a gas-tight metal-supported oxygen transport membrane structure.
Journal: Journal of the European Ceramic Society - Volume 33, Issue 2, February 2013, Pages 287–296