Evolution of structure during the oxidation of zirconium diboride–silicon carbide in air up to 1500 °C
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
The structures that developed as dense ZrB2–SiC ceramics were heated to 1500 °C in air were characterized using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction. The oxidation behavior was also studied using thermal gravimetric analysis (TGA). Below 1200 °C, a protective B2O3-rich scale was observed on the surface. At 1200 °C and above, the B2O3 evaporated and the SiO2-rich scale that formed was stable up to at least 1500 °C. Beneath the surface, layers that were rich in zirconium oxide, and from which the silicon carbide had been partially depleted, were observed. The observations were consistent with the oxidation sequence recorded by thermal gravimetric analysis.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of the European Ceramic Society - Volume 27, Issue 6, 2007, Pages 2495–2501
Journal: Journal of the European Ceramic Society - Volume 27, Issue 6, 2007, Pages 2495–2501
نویسندگان
Alireza Rezaie, William G. Fahrenholtz, Gregory E. Hilmas,