Fabrication of barium titanate nanoparticles/poly (methylmethacrylate) composite films by a combination of deposition process and spin-coating technique

The present work proposes a method for fabricating poly(methylmethacrylate) (PMMA) film containing barium titanate (BT) nanoparticles (BT/PMMA film). BT particles with an average size of 77.6 ± 30.5 nm and a crystal size of 28.1 nm were synthesized by adding sodium hydroxide aqueous solution to titanium tetraisopropoxide/acetylacetone/i-propanol solution suspending barium hydroxide. A sodium glass plate, of which surface was modified with polyvinylpyrrolidone, was immersed into water suspending the BT particles, which resulted in deposition of the BT particles on the plate. A BT/PMMA film was fabricated by twice performance of a process composed of spin-coating of N-methyl-2-pyrrolidone (NMP) dissolving PMMA on the plate, and then drying the coated plate in the atmosphere at room temperature. Spin-coating of a PMMA/NMP solution with a PMMA concentration of 150 g/L at a rotating speed of 5000 rpm provided fabrication of a BT/PMMA film with a BT volume fraction of 35.5%, a thickness of ca. 300 nm, and a transmittance of ca. 90% in the visible light region.