• Red-light-emitting La4Ti9O24:Eu3+ phosphor was obtained from sol–gel precursors.
• Under 465 nm excitation, the phosphor exhibits strong red emission at 613 nm.
• Doping with either Si4+ or Bi3+ enhances emission intensity of the phosphor.
• The phosphor could be candidate for color mixing in white light-emitting diode.
Eu3+ activated La4Ti9O24 phosphors were prepared by firing precursors from sol–gel method. Under the excitation of 465 nm light, the phosphor with optimized concentration at 3% shows strong red light emission peaked at 613 nm with high color purity owing to 5D0 → 7F2 emission of Eu3+. When adequate amount of either Si4+ or Bi3+ is incorporated in La4Ti9O24 host, the photoluminescence intensity of as-prepared La4Ti9O24:Eu3+ phosphor can be enhanced by 12% and 19.4%, respectively. As the (La0.97Eu0.03)4Ti9O24 is pumped with blue-light, high purity red emission with chromaticity coordinates (0.6380, 0.3616) is achieved at the optimized condition. This phosphor might be applied in the solid-state white light emission devices based on blue light-emitting diodes.
Figure optionsDownload as PowerPoint slide
Journal: Materials Research Bulletin - Volume 51, March 2014, Pages 185–188