• A novel octapod Pt nanocrystals different from the common octapod were obtained.
• The use of KI was crucial to the formation of the novel Pt octapods.
• Microwave was readily employed in controlled synthesis of the novel Pt octapods.
Microwave was employed in the shape-controlled synthesis of Pt nanoparticles. Novel octapod Pt nanocrystals enclosed with (1 1 1) facets were readily synthesized with H2PtCl6 as a precursor, tetraethylene glycol (TEG) as both a solvent and a reducing agent, polyvinylpyrrolidone (PVP) as a stabilizer in the presence of an appropriate amount of KI under microwave irradiation for 140 s. The as-prepared Pt nanocrystals displayed a unique octapod nanostructure with five little mastoids in each concave center and exhibited higher electrocatalytic activity than commercial Pt black in the electro-oxidations of methanol and formic acid. The results demonstrated that the use of KI was crucial to the formation of Pt octapods. KI determined the formation of the novel octapod Pt nanocrystals by tuning up the reduction kinetics and adsorbing on the surfaces of growing Pt nanoparticles. The optimum molar ratio of H2PtCl6/KI/PVP was 1/30/45.
Under microwave irradiation, novel octapod Pt nanocrystals were synthesized by reducing H2PtCl6 in TEG with PVP as a stabilizer. The as-prepared Pt nanocrystals displayed a unique octapod nanostructure with five little mastoids in each concave center. The use of KI was crucial to the formation of novel Pt octapods. Novel Octapod Platinum Nanocrystals.Figure optionsDownload as PowerPoint slide
Journal: Materials Research Bulletin - Volume 49, January 2014, Pages 413–419