The nanocomposites of Y3Al5O12:Nd3+ (YAG:Nd) incorporated in borate glass were obtained. The single phase of YAG:Nd nanocrystals were obtained by sol–gel method. The borate glass was melted first and ground up then mixed with the nanocrystals. The samples were formed into pellets under pressure and were annealed in temperatures from the range 550–800 °C. The X-ray diffraction patterns show that together with increasing the temperature the contribution of Y3Al5O12 phase decreases and the new YBa3B9O19 phase is observed. The luminescence measurements indicates that the band structures and distribution of band intensities of glass-YAG:Nd nanocrystal composites depends crucially on annealing temperature.
Figure optionsDownload as PowerPoint slideHighlights
► The mixture of borate glass powder and YAG:5%Nd3+ nanocrystals was prepared.
► The samples were formed into pallets and annealed at different temperatures.
► The luminescence properties of composites depends crucially on annealing temperature.
Journal: Materials Research Bulletin - Volume 46, Issue 10, October 2011, Pages 1566–1570