Hot-pressed chromium doped zinc sulfide infrared transparent ceramics

The present study, for the first time, reports the successful consolidation of chromium doped zinc sulfide (ZnS) polycrystalline infrared (IR) transparent ceramics (maximum transmittance of 67% at 11.6 μm) via hot pressing under vacuum. The phase composition of the as-sintered Cr2+:ZnS ceramics was determined to be primarily cubic ZnS sphalerite, with a minor amount of hexagonal ZnS wurtzite. Scanning electron microscopy (SEM) observation of the sintered ceramics showed a highly consolidated microstructure. IR absorption and photoluminescence measurements revealed that the Cr2+ ions are tetrahedrally coordinated within the ZnS host lattice.