Effect of dominant diffusion process on cavitation behavior in superplastic Mg–Al–Zn alloy

Cavities were formed in the random boundaries of superplastic magnesium alloys due to higher boundary energy. The cavity growth rate of the fine-grained alloy (dominant diffusion process: grain boundary diffusion) was lower than that of the coarse-grained alloy (lattice diffusion) during superplastic flow.