Synthesis and fabrication of Y2O3:Tb3+ and Y2O3:Eu3+ thin films for electroluminescent applications: Optical and structural characteristics
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
مواد الکترونیکی، نوری و مغناطیسی
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Terbium, europium and yttrium β diketonates have been synthesized from acetylacetone and inorganic metal salts and used as precursors for the deposition of Tb3+ or Eu3+ doped Y2O3 polycrystalline films by the ultrasonic spray pyrolysis technique. The films were deposited on c-Si substrates at temperatures in the 400-550 °C range. The optical and structural characterization of these films as a function of substrate temperature and Tb3+ and Eu3+ concentration was carried out by means of photoluminescence (PL), cathodoluminescence (CL), infrared (IR), ellipsometry, and UV-visible spectroscopy and atomic force microscopy (AFM), energy dispersive spectroscopy (EDS) and X ray diffraction (XRD) measurements respectively. The PL intensity from these films was found to depend on deposition temperature. Films deposited above 450 °C exhibited the characteristic PL peaks associated with either Tb3+ or Eu3+ intra electronic energy levels transitions. The most intense PL emission was found for dopant concentration of 10 at% for Tb3+ and at 8 at% for Eu3+ ions into precursor solution. In both cases concentration quenching of the PL emission was observed for concentrations above these values. The films had a refractive index (1.81), low average surface roughness (â¼62 Ã
) and a UV-Vis. transmission of the order of 90 %T.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Chemistry and Physics - Volumes 149â150, 15 January 2015, Pages 34-42
Journal: Materials Chemistry and Physics - Volumes 149â150, 15 January 2015, Pages 34-42
نویسندگان
G. Alarcón-Flores, M. GarcÃa-Hipólito, M. Aguilar-Frutis, S. Carmona-Téllez, R. Martinez-Martinez, M.P. Campos-Arias, E. Zaleta-Alejandre, C. Falcony,