Distortion and residual stress measurements of induction hardened AISI 4340 discs
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
مواد الکترونیکی، نوری و مغناطیسی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Distortion and residual stress measurements of induction hardened AISI 4340 discs Distortion and residual stress measurements of induction hardened AISI 4340 discs](/preview/png/1522374.png)
چکیده انگلیسی
10 Induction hardened discs with two initial hardness levels were used for exploring the influences of the variation of initial hardness as well as induction hardening (IH) recipes on the heat treatment distortions and hardening depth. The results show that for the same initial hardness, the larger the energy input, the higher the distortion size as well as the hardening depth. For a given induction hardening recipe, the increase in initial hardness leads to a deeper hardening depth but a smaller distortion. One disc was selected for the residual stress investigation in three orthogonal directions by neutron diffraction (ND). The corresponding stress-free lattice spacing d0 was measured from the same material using both ND and X-ray diffraction (XRD) methods. The ND results show that the variation of d0 in the hardened layer is significant and should be taken into account for stress calculation. However, regarding the core region, the d0 value measured by XRD is more reliable. Accordingly, a combination of the ND-measured d0 profiles in the hardened layer and the XRD-measured d0 value in the core was adopted for the determination of residual stress distributions.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Chemistry and Physics - Volume 142, Issue 1, 15 October 2013, Pages 248-258
Journal: Materials Chemistry and Physics - Volume 142, Issue 1, 15 October 2013, Pages 248-258
نویسندگان
J. Yi, M. Gharghouri, P. Bocher, M. Medraj,