Influence of modifier oxides on some physical properties of antimony borate glass system doped with V2O5

Three series of glasses, of the composition 20 MO (M = Ca, Pb, Zn)–40 Sb2O3–(40 − x) B2O3:xV2O5, with six values of x ranging from 0 to 1 mol% were prepared. The samples were characterized by X-ray diffraction, scanning electron microscopy, EDS and differential scanning calorimetric techniques. The comparison of DSC data among the three series has indicated high glass forming ability for ZnO mixed glasses. Dielectric properties over a range of frequency and temperature, optical absorption, ESR spectra at room temperature and IR spectra have been investigated. The variations observed in all these properties due to different modifiers as a function of the concentration of V2O5 have been analyzed in the light of different oxidation states and environment of vanadyl ions in these glasses. The analysis of these results indicated that the ZnO mixed glasses are more stable against devetrification and possess high insulating strength when compared with PbO and CaO mixed glasses.