Effect of B2O3 on the aqueous tape casting and microwave properties of Li2O–Nb2O5–TiO2 ceramics

The effect of B2O3 addition on the aqueous tape casting, sintering, microstructure and microwave dielectric properties of Li2O–Nb2O5–TiO2 ceramics has been investigated. The tape casting slurries exhibit a typical shear-thinning behavior without thixotropy, but the addition of B2O3 increases the viscosity of the slurries significantly. It was found that doping of B2O3 can decrease the tensile strength, strain to failure and density of the green tapes. The sintering temperature could be lowed down to 900 °C with the addition of 2 wt% B2O3 due to the liquid phase effect. No secondary phase is observed. The addition of B2O3 does not induce much degradation on the microwave dielectric properties. Optimum microwave dielectric properties of εr=67, Q×f=6560 GHz are obtained for Li2O–Nb2O5–TiO2 ceramics containing 2 wt% B2O3 sintered at 900 °C. It represents that the ceramics could be promising for multilayer low-temperature co-fired ceramics (LTCC) application.