Crystallographic study of Si and ZrN coated U-Mo atomised particles and of their interaction with al under thermal annealing

It was found for the U-Mo particles coated with ZrN (thickness 1 μm), that the layer is crystalline, and exhibits lower density than the theoretical one. Fuel plate manufacturing does not strongly influence these crystallographic features. For the U-Mo particles coated with Si (thickness 0.6 μm), the measurements of the as received material suggest an amorphous state of the deposited layer. Fuel plate manufacturing strongly modifies its composition: Si reacts with the U-Mo particles and the Al matrix to grow U(Al, Si)3 and U3Si5 phases. Finally both coatings have shown excellent performances under thermal treatment by limiting drastically the U-Mo/Al interdiffusion.