Property change of advanced tungsten alloys due to neutron irradiation

This study investigates the effect of neutron irradiation on the functional properties of pure tungsten (W) and advanced tungsten alloys (e.g., lanthanum (La)-doped W, potassium (K)-doped W, and ultra-fine-grained (UFG) W-TiC alloys) tested in the Japan Materials Testing Reactor (JMTR) or experimental fast reactor Joyo. The irradiation temperature and damage were in the range 804-1073 K and 0.15-0.47 dpa, respectively. TEM images of all samples after 0.42 dpa irradiation at 1023 K showed voids, black dots, and dislocation loops, indicating that similar damage structures were formed in pure W, La-doped W, K-doped W, and UFG W-0.5 wt% TiC. The electrical resistivity of all specimens increased following neutron irradiation. Nearly identical electrical resistivity and irradiation hardening were observed in pure W, La-doped W, and K-doped W. The electrical resistivity of UFG W-TiC was higher than that of other specimens before and after irradiation, which may be attributed to its ultra-fine-grain structure, as well as the presence of impurities introduced during the alloying process. Compared to the other specimens, the UFG W-TiC was more resistant to irradiation hardening.