Comparison of delayed hydride cracking behavior of two zirconium alloys

Delayed hydride cracking (DHC) is an important failure mechanism that may occur in Zr alloys during service in water-cooled reactors. Two conditions must be attained to initiate DHC from a crack: the stress intensity factor must be higher than a threshold value called KIH and, hydrogen concentration must exceed a critical value. Currently the pressure tubes for CANDU reactor are fabricated from Zr–2.5Nb. In this paper the critical hydrogen concentration for DHC and the crack velocity of a developmental pressure tube, Excel, was evaluated and compared with that of Zr–2.5Nb. The DHC velocity values measured in Excel were higher than usually reported in Zr–2.5Nb. Due to the higher hydrogen solubility limits in Excel, its critical hydrogen concentration for DHC initiation is 10–50 wppm over that of Zr–2.5Nb in the range of 150–300 °C.