Defects and microstructural evolution of proton irradiated titanium carbide

The predominant irradiation induced aggregate defects found by high resolution TEM and diffraction contrast TEM were interstitial Frank-type loops, while unfaulted loops were also identified. By monitoring the loop sizes and densities and accounting for the interstitials which formed the loops, a marked increase in vacancy point defect mobility was observed around 800 °C.