Corrosion behavior of plasma-sprayed Al2O3–Cr2O3 coatings in hot lithium molten salt

In this study, hot corrosion studies were performed on bare as well as coated superalloy specimens after exposure to molten lithium chloride environment at 675 °C for 216 h under an oxidizing atmosphere. The substrates of the IN713LC superalloy specimens were sprayed with an aluminized NiCrAlY bond coat and then with an Al2O3–Cr2O3 top coat. The as-coated and tested specimens were examined by optical microscopy (OM), scanning electron microscopy (SEM)/X-ray energy dispersive spectrometry (EDS) and X-ray diffraction (XRD), respectively. The bare superalloy reveals an obvious weight loss, and the scale formed on the surface of the bare superalloy was spalled due to the rapid scale growth and thermal stress. The top coatings showed a much better hot corrosion resistance in the presence of LiCl–3 wt.% Li2O molten salt when compared with those of the uncoated superalloy and the aluminized bond coatings. These coatings have been found to be beneficial for increasing to the hot corrosion resistance of the structural materials for handling high temperature lithium molten salts.