Microstructural investigation, using small-angle neutron scattering (SANS), of Optifer steel after low dose neutron irradiation and subsequent high temperature tempering

The microstructural effect of low dose neutron irradiation and subsequent high temperature tempering in the reduced activation ferritic/martensitic steel Optifer (9.3 Cr, 0.1 C, 0.50 Mn, 0.26 V, 0.96 W, 0.66 Ta, Fe bal wt%) has been studied using small-angle neutron scattering (SANS). The investigated Optifer samples had been neutron irradiated, at 250 °C, to dose levels of 0.8 dpa and 2.4 dpa. Some of them underwent 2 h tempering at 770 °C after the irradiation. The SANS measurements were carried out at the D22 instrument of the High Flux Reactor at the Institut Max von Laue – Paul Langevin, Grenoble, France. The differences observed in nuclear and magnetic SANS cross-sections after subtraction of the reference sample from the irradiated one suggest that the irradiation and the subsequent post-irradiation tempering produce the growth of non-magnetic defects, tentatively identified as microvoids.