![عکس صفحه اول مقاله: Formation of bulk metallic glass in situ nanocomposite in (Cu50Zr43Al7)99Si1 alloy Formation of bulk metallic glass in situ nanocomposite in (Cu50Zr43Al7)99Si1 alloy](/preview/png/1576880.png)
The structure and mechanical properties of the bulk (Cu50Zr43Al7)99Si1 (at.%) rods with different diameters prepared by copper mold casting are investigated. It was found that the alloy with diameter of 2 mm has a fully glassy structure. The nanocrystals with the sizes ranging from 2 to 10 nm distributed in the glassy matrix for the alloy rod with a diameter of 3 mm, and the successful synthesis of the (Cu50Zr43Al7)99Si1 bulk metallic glass in situ nanocomposite was obtained. High compressive strength of 1969 MPa and limited plastic strain of less than 1% were obtained for the 2 mm (Cu50Zr43Al7)99Si1 glassy rod. For the 3 mm alloy rod, the compressive strength and plastic strain are 1835 MPa and 10%, respectively. The CuZr nanocrystalline phase precipitated from the 3 mm (Cu50Zr43Al7)99Si1 rod shows evident plastic deformation, which contributes to the high ductility of the (Cu50Zr43Al7)99Si1 bulk metallic glass in situ nanocomposites.
Figure optionsDownload as PowerPoint slideHighlights
► Formation of bulk metallic glass in situ nanocomposite in (Cu50Zr43Al7)99Si1 alloy by copper mold casting.
► The CuZr nanocrystals distributed in the glassy matrix with a diameter of 3 mm.
► The 3 mm rod exhibits high compressive strength of 1835 MPa and high ductility of 10%.
► The 2 mm rod has a fully glassy structure with limited plastic strain of less than 1%.
► The mechanisms for the formation and deformation of the BMG nanocomposite are discussed.
Journal: Materials Science and Engineering: A - Volume 553, 15 September 2012, Pages 10–13