Magnetic and magnetocaloric properties in La0.7Ca0.3âxNaxMnO3 exhibiting first-order and second-order magnetic phase transitions
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Magnetic and magnetocaloric properties in La0.7Ca0.3âxNaxMnO3 exhibiting first-order and second-order magnetic phase transitions Magnetic and magnetocaloric properties in La0.7Ca0.3âxNaxMnO3 exhibiting first-order and second-order magnetic phase transitions](/preview/png/1605810.png)
چکیده انگلیسی
Polycrystalline orthorhombic samples La0.7Ca0.3âxNaxMnO3 (x = 0-0.09) were prepared by solid-state reaction. The study of magnetic properties revealed that the ferromagnetic-paramagnetic (FM-PM) transition temperature (TC) increases from 255 to about 271 K with increasing Na-doping content (x) from 0 to 0.09, respectively. Around the TC, we have found the samples showing a large magnetocaloric (MC) effect with maximum values of magnetic entropy change (|ÎSmax|) of 7-8 J kgâ1 Kâ1 and relative cooling power RCP = 232-236 J/kg for the samples x = 0.03-0.09 in a magnetic-field interval ÎH = 40 kOe. Detailed analyses of isothermal magnetization data M(T, H) based on Banerjee's criteria indicated a first-to-second-order magnetic-phase transformation taking place at a threshold Na-doping concentration xc â 0.06. This could also be observed clearly from the feature of entropy universal curves. An assessment of the magnetic-ordering exponent N = dLn|ÎSm|/dLnH demonstrates an existence of short-range magnetic order in the samples. We believe that the changes of the magnetic properties and MC effect in La0.7Ca0.3âxNaxMnO3 caused by Na doping are related to the changes in the structural parameters and Mn4+/Mn3+ ratio, which are confirmed by the geometrical and electronic analyses based on X-ray diffraction and X-ray absorption fine structure.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 676, 15 August 2016, Pages 305-312
Journal: Journal of Alloys and Compounds - Volume 676, 15 August 2016, Pages 305-312
نویسندگان
T.A. Ho, N.T. Dang, The-Long Phan, D.S. Yang, B.W. Lee, S.C. Yu,