• LaB6 powder was added to sintered and hot worked Ti and Ti–6Al–4V alloy.
• TiB whiskers and La2O3 dispersoids formed in the microstructure.
• Different alignments of TiBw led to a variation in mechanical properties.
• Hot working caused severe deformation and re-alignment of TiBw.
• An addition of LaB6 is better than pure boron additions.
A trace amount of LaB6 powder was added to P/M Ti and Ti–6Al–4V alloy to improve mechanical properties and refine the microstructure. After sintering, TiB whiskers and La2O3 dispersoids had formed in the microstructure. In a CP Ti alloy, the generation of secondary phases leads to a much refined microstructure, but the alignment of TiB whiskers led to a variation in mechanical properties. Open die forging (ODF) or powder compact extrusion (PCE) was carried out on sintered Ti–6Al–4V alloy to further improve the mechanical properties. This caused severe deformation and re-alignment of the TiB whiskers. Comparing the properties of hot worked Ti–6Al–4V alloy and Ti–6Al–4V alloy with boron additions, an addition of LaB6 leads to slightly lower strength but gives significant better ductility.
Journal: Journal of Alloys and Compounds - Volume 674, 25 July 2016, Pages 116–124