Nano-sized Li4Ti5O12/C anode material with ultrafast charge/discharge capability for lithium ion batteries

• One step synthesis of LTO/C composite with low cost sucrose as carbon source.
• Nanosized LTO composite (13 nm) with high electronic conductivity (10−4 S cm−1).
• Outstanding ultrafast charge/discharge performance.

Nano-structured Li4Ti5O12 crystals coated with carbon layer are in situ synthesized via one-step liquid process taking advantage of low-cost sucrose as carbon source in this work. The as-prepared LTO/C particles present much larger specific surface area (58 m2 g−1) relative to the value of pure LTO, with a size around 13 nm in average. Its electronic conductivity of 6.56 × 10−4 S cm−1 is over three orders of magnitude higher than the pure one. The composite anode displays a distinguished electrochemical charge/discharge performance, especially, quite high rate capability along with a stable cyclability. It delivers the initial discharge specific capacities of 156.7 and 142.1 mA h g−1 at 40C and 60C respectively, and remains the values of 114.2 and 98.1 mA h g−1 after 200 cycles. Furthermore, a capacity of 132.8 mA h g−1 is delivered even at an 80C rate and the value of 82.7 mA h g−1 can be maintained after 200 cycles. The ultrafast charge/discharge capability may be attributed to the shorten Li+ transport path in the nanosized composite and the enlarged access area with electrolyte. Additionally, the carbon coating may provide an effective conductive network among the particles promoting charge transfer.

Figure optionsDownload as PowerPoint slide